# NTSB investigations: CFM International CFM56 series: Aircraft structural failure

NTSB aviation accident and incident investigations since 1962: the probable cause, findings, aircraft, crew, weather and docket of each, linked to the FAA registry and the FAA’s own reports.

## Latest cases

- [NTSB DCA12IA113](https://openairdocs.org/ntsb/DCA12IA113.md): Boeing 737-3H4 · El Paso, TX · Incident · No injuries · Incident investigation · Final report · Jul 27, 2012 · N379SW · Minor damage
  > the rupture of the nose landing gear hydraulic line that resulted from abrasions due to contact with the nose landing gear tire. Contributing to the incident was the incorrect installation of union and restrictor on the actuator.
- [NTSB ENG10IA016](https://openairdocs.org/ntsb/ENG10IA016.md): Douglas DC8 · Cincinnati (CVG), OH · Incident · No injuries · Incident investigation · Final report · Jan 7, 2010 · N803DH · Minor damage
  > Failure of the NLG cylinder occurred by intergranular rupture; coincidental to a chrome plating crack. The failure origin occurred along the inner surface of the cylinder and then propagated by stress corrosion cracking to the outer surface. A secondary crack…
- [NTSB ENG09IA014](https://openairdocs.org/ntsb/ENG09IA014.md): Boeing 737 · Los Angeles, CA · Incident · No injuries · Incident investigation · Final report · Sep 8, 2009 · N670SW · Minor damage
  > The failure of the right main landing gear inboard axle due to fatigue cracking as a result of fretting damage in one of the brake mounting bolt holes.
- [NTSB ENG09IA009](https://openairdocs.org/ntsb/ENG09IA009.md): Boeing 737-3B7 · Charlotte (CLT), NC · Incident · No injuries · Incident investigation · Final report · Jul 15, 2009 · N506AU · Minor damage
  > The failure of the left hand main landing gear was caused by heat induced cracks resulting from abusive grinding/polishing of the chrome plate that was applied during the last overhaul.
- [NTSB DCA09FA065](https://openairdocs.org/ntsb/DCA09FA065.md): Boeing 737 · Charleston, WV · Accident · No injuries · Field investigation · Final report · Jul 13, 2009 · N387SW · Substantial damage
  > Fuselage skin failure due to preexisting fatigue at a chemically milled step.
- [NTSB ENG08IA051](https://openairdocs.org/ntsb/ENG08IA051.md): Boeing 737 · Phoenix (PHX), AZ · Incident · No injuries · Incident investigation · Final report · Jun 27, 2008 · N514AU · Minor damage
  > The failure of the MLG was due to cracking in the cylinder wall resulting from a fatigue mechanism which initiated at, and near the inner diameter (ID) surface, with propagation through the wall toward the outer diameter(OD) surface. Crack initiation was due…

## The whole list in SQL

Runs in DuckDB 1.2 or later on the release's Parquet files over HTTPS:

```sql
SELECT c."ntsbNumber", c."eventDate", c."eventType", c."eventCity", c."eventStateOrRegion", a.n_number, a."aircraftMake", a."aircraftModel", c."highestInjuryLevel", c."totalFatal", c."completionStatus", c.report_url
FROM 'https://openairdocs.org/data/latest/ntsb_case_detail.parquet' c LEFT JOIN 'https://openairdocs.org/data/latest/ntsb_aircrafts.parquet' a ON a.case_mkey = c."mKey" AND a.position = 1
WHERE c."mKey" IN (SELECT x.case_mkey FROM 'https://openairdocs.org/data/latest/ntsb_aircrafts.parquet' x WHERE x.engine_model_code IN ('13802')
    AND EXISTS (SELECT 1 FROM 'https://openairdocs.org/data/latest/ntsb_events.parquet' e WHERE e.case_mkey = x.case_mkey AND e.aircrafts_position = x.position AND e."isDefiningEvent" AND e."tier2Number" = '337'))
ORDER BY c."eventDate" DESC, c."ntsbNumber" DESC
```

This list as a web page: https://openairdocs.org/ntsb-events/337/cases?engine=13802

---
OpenAirDocs.org is an independent research project of [Contrail Labs](https://contraillabs.com/). It is not affiliated with the FAA or the NTSB. Source documents are U.S. government works in the public domain.