N203CM, cancelled Oct 31, 2024

Service difficulty reports · 19

Matched to this aircraft by N-number and event date, checked against the reported serial number, make and model. Newest first.

Query with SQL
duckdb -csv -c "SELECT sdr_id, difficulty_date, n_number, aircraft_make, aircraft_model, part_name, part_condition, jasc_code, discrepancy
  FROM 'https://openairdocs.org/data/latest/faa_service_difficulty_report.parquet'
  WHERE n_number = 'N203CM' AND deregistration_id = 'N203CM-2024-10-31'
  ORDER BY difficulty_date DESC"

Prints the whole list as CSV. It reads the release’s Parquet files over HTTPS, so there’s nothing to download first. Install DuckDB to run it.

SDR 2024FA0000569Skin · dentedREWPAIR - SECTION 41 - DENT - RH FUSELAGE SKIN BETWEEN STA 303 AND 325 AND BETWEEN STR 35R-36R.Aug 6, 2024 · N203CM · Boeing 767375 · Fuselage Main, Plate/SkinSDR MK1Y202207060018Housing · corrodedL/H WING - MAIN FUEL TANK FUEL BOOST PUMP HOUSING REPAIRS - DURING MAINTENANCE INSPECTION AT IAI' CORROSIN WAS FOUND ON THE INNER FACE OF THE FUEL BOOST PUMP HOUSING ATTER REMOVING THE FWD FUEL BOOST PUMP SHUTOFF SLEEVEJul 6, 2022 · N203CM · Boeing 767323 · Fuel Boost PumpSDR MK1Y20220706017Repair · discoveredENG@ 2 - STRUT FAIRING - OUTBRD SIDE - NAC STA 304.5 - NAC STA 307.9 - - DURRING MAINTENANCE AT IAI - EXISTING UNDOCUMENTED REPAIR WAS FOUND ON STRUT OF ENGINE #2, OUTBRD SIDE FAIRUNG SKIN.Jul 6, 2022 · N203CM · Boeing 767323 · Nacelle/Pylon StructureSDR MK1Y20220706016Housing · corrodedL/H WING - MAIN FUEL TANK FUEL BOOST PUMP HOSING REPAIRS - DURING MAINTENANCE INSPECTION AT IAI, CORROSION WAS FOUND ON THE INNER FACE OF THE FUEL BOOST PUMP HOUSING AFTER REMOVING THE AFT FUEL BOOST PUMP SHUTOFF SLEEVE.Jul 6, 2022 · N203CM · Boeing 767323 · Fuel Boost PumpSDR MK1Y20220706015Skin Panel · crackedPROBLEM DESCRIPTION: PYLON #1, STRUT SIDE SKIN PANEL, PANEL 432AL, NAC 233,WL 143: FOUND EXTENDED CRACK BEYOND RIVET AT OUTER SKIN OF THE PYLON BY 1.8” IN LENGTH FROM THE CUTOUT OF PANEL 432AL.Jul 6, 2022 · N203CM · Boeing 767323 · Nacelle/Pylon, Plate/SkinSDR MK1Y20220706014Skin Panel · crackedPYLON # 2, OUTER SKIN PANEL 432AL, NAC 233, WL 143: FOUND EXTENDED CRACK BEYOND RIVET AT OUTER SKIN OF THE PYLON BY 2.5” IN LENGTH FROM THE CUTOUT OF PANEL 432AL.Jul 6, 2022 · N203CM · Boeing 767323 · Nacelle/Pylon, Plate/SkinSDR MK1Y20220706013Skin · out of limitsEXTERNAL FUSELAGE SKIN, STA 226 – STA 347, STR-28L – STR-29L: NRC M0143-EXTERNAL FUSELAGE SKIN BS 226.5 AND 2.2” BELOW STR 29L: SKIN THICKNESS: 0.080”. REMOVED FASTENER: JO-BOLT 0.185” DIA.OS-1 EXISTING REPAIR WASHER: DIAMETR: 0.580”, THICKNESS: 0.065”. NRC MJul 6, 2022 · N203CM · Boeing 767323 · Fuselage Main, Plate/SkinSDR MK1Y20220706012Repair · discoveredR/H HORIZONTAL STABILIZER – UPPER SKIN: DURING MAINTENANCE PRACTICES AT IAI IN TLV, AN EXISTING UNDOCUMENTED REPAIR WAS FOUND ON R/H HORIZONTAL STABILIZER UPPER SKIN. THE SKIN IS MADE FROM ALCLAD 7075-T6 1.100” IN THICK. THE REPAIR FOUND CONSISTS IN ONE DOUBLEJul 6, 2022 · N203CM · Boeing 767323 · Empennage StructureSDR MK1Y20220706011Repair · discoveredR/H MLG SHOCK STRUT DOOR:DURING MAINTENANCE INSPECTION AT IAI, EXISTING UNDOCUMENTED REPAIR WAS FOUND ON R/H MLG SHOCK STRUT DOORJul 6, 2022 · N203CM · Boeing 767323 · DoorsSDR MK1Y20220706010Repair · discoveredSTRUT # 2, INBD SIDE, SKIN 313T3310: DURING MAINTENANCE PRACTICES AT IAI IN TLV, AN EXISTING UNDOCUMENTED DOUBLER REPAIR WAS FOUND ON STRUT # 2 INBD SIDE, ON SKIN 313T3310. THE SKIN IS MADE FROM TWO BONDED SKINS OF ALCLAD 2024-T3 0.063” AND 0.040” IN THICKNESSJul 6, 2022 · N203CM · Boeing 767323 · Nacelle/Pylon StructureSDR MK1Y20220706009Skin · damagedDURING MAINTENANCE INSPECTION LIGHTNING STRIKES WERE DISCOVERED ON THE EXTERNAL FUSELAGE SKIN BETWEEN STA 212 AND STA 303, STR-29L – STR-30L. THE LIGHTNING STRIKES WERE BLENDED OUT. THE BLEND OUT AREA IS LOCATED COMMON TO THE EXISTING FASTENERS. AFTER INSPECTIJul 6, 2022 · N203CM · Boeing 767323 · Fuselage Main, Plate/SkinSDR MK1Y20220706008Skin Panel · corrodedCENTER WING SECTION, UPPER CHORD AREA, STA 955, RBL 11.00: DURING CONVERSION WORK AT IAI, A CORROSION WAS FOUND AT DATUM LOCATION ON SKIN PANEL NO.1 OF CENTER WING, PRESSURE DECK WEB, AND UPPER CHORD OF REAR SPAR OF CENTER WING. THE SKIN AND WEB WERE BLENDED AJul 6, 2022 · N203CM · Boeing 767323 · Fuselage Structure (General)SDR MK1Y20220706007Repair · discovered: ENGINE #1, STRUT FAIRING, INBD SIDE, NAC STA 304.1 – NAC STA 311.1: DURING MAINTENANCE INSPECTION AT IAI, THE EXISTING UNDOCUMENTED REPAIR WAS FOUND ON THE STRUT FAIRING AT DATUM LOCATION.Jul 6, 2022 · N203CM · Boeing 767323 · Nacelle/Pylon StructureSDR MK1Y20220706006Skin · damagedDURING MAINTENANCE INSPECTION LIGHTNING STRIKES WERE DISCOVERED ON THE EXTERNAL FUSELAGE SKIN BETWEEN STA 368 AND STA 412, STR-28L – STR-30L. THE LIGHTNING STRIKES WERE BLENDED OUT. THE BLEND OUT ARE LOCATED COMMON TO THE EXISTING FASTENERS. AFTJul 6, 2022 · N203CM · Boeing 767323 · Fuselage Structure (General)SDR MK1Y20220706005Skin · scratched: EXTERNAL FUSELAGE SKIN, STA 1487, STR-22L – STR-23L: DURING MAINTENANCE INSPECTION AT IAI, SCRATCHES WERE FOUND AT DATUM LOCATION. THE DAMAGE WAS BLENDED OUT AND FOUND WITHIN LIMITS, HOWEVER, THE BLEND OUT IS AMONG THE FASTENERS THAT PROHIBITED PER SRM 53-0Jul 6, 2022 · N203CM · Boeing 767323 · Fuselage Main, Plate/SkinSDR MK1Y20220706004Repair · discoveredENGINE #2, STRUT ACCESS PANEL 446BR, NAC STA 249 – NAC STA 253: DURING MAINTENANCE INSPECTION AT IAI, EXISTING UNDOCUMENTED REPAIR WAS FOUND ON ENGINE #2, STRUT, ACCESS PANEL NO. 446BR.Jul 6, 2022 · N203CM · Boeing 767323 · Nacelle/Pylon StructureSDR MK1Y20220706003Stub Frame · crackedTHE CRACK FOUND IN THE TRANSITION RADIUS OF THE RIGHT FUSELAGE FRAME STUB BEAM LOCATED STA 883.5 AND RBL 89. THE CRACK WAS FOUND DURING A REPETITIVE HFEC SURFACE INSPECTION IAW BOEING SERVICE BULLETIN 767-53A0209, AS MANDATED BY AIRWORTHINESS DIRECTIVE 2012-22Jul 6, 2022 · N203CM · Boeing 767323 · Fuselage Main, FrameSDR MK1Y20220706002Stub Frame · crackedTHE CRACK FOUND IN THE TRANSITION RADIUS OF THE LEFT FUSELAGE FRAME STUB BEAM LOCATED STA 859.5 AND LBL 89. THE CRACK WAS FOUND DURING A REPETITIVE HFEC SURFACE INSPECTION IAW BOEING SERVICE BULLETIN 767-53A0209, AS MANDATED BY AIRWORTHINESS DIRECTIVE 2012-22-Jul 6, 2022 · N203CM · Boeing 767323 · Fuselage Main, FrameSDR MK1Y20220706001Skin Panel · corrodedCENTER WING, UPPER SKIN, PANEL NO. 1, STA 955, LBL 74.00: DURING MAINTENANCE INSPECTION AT IAI, CORROSION WAS FOUND AT DATUM LOCATION. THE DAMAGE WAS BLENDED OUT AND FOUND WITHIN LIMITS, HOWEVER, THE BLEND OUT IS AMONG THE FASTENERS THAT PROHIBITED PER SRM 53-Jul 6, 2022 · N203CM · Boeing 767323 · Wing, Plate/Skin
Back to N203CM, cancelled Oct 31, 2024