JASC 2571
Service difficulty reports · 66
Reports filed under 2571 · Battery Box Structure, newest first.
Query with SQL
duckdb -csv -c "SELECT sdr_id, difficulty_date, n_number, aircraft_make, aircraft_model, part_name, part_condition, jasc_code, discrepancy FROM 'https://openairdocs.org/data/latest/faa_service_difficulty_report.parquet' WHERE jasc_code = '2571' ORDER BY difficulty_date DESC"
Prints the whole list as CSV. It reads the release’s Parquet files over HTTPS, so there’s nothing to download first. Install DuckDB to run it.
SELECT sdr_id, difficulty_date, n_number, aircraft_make, aircraft_model, part_name, part_condition, jasc_code, discrepancy FROM 'https://openairdocs.org/data/latest/faa_service_difficulty_report.parquet' WHERE jasc_code = '2571' ORDER BY difficulty_date DESC
Run it at the DuckDB prompt, or in any tool that reads Parquet over HTTPS. More ways to query the release are on Use the data.
SDR 20000920SH016Support Bracket · crackedON INSPECTION OF AIRCRAFT, FOUND LEFT AND RIGHT BATTERY BOX SUPPORTS CRACKED IN BEND RADIUS, P/N 0712059-1. 24V BATTERY LOCATED IN TAIL SECTION OF AIRCRAFT. NOTE: THIS PROBLEM HAS BEEN FOUND IN OTHER 182R''S. (X)SDR 98ZZZX2809Battery Box · corrodedDURING ANNUAL INSPECTION, RIVETS IN BOTTOM OF BOX WERE FOUND CORRODED AND MISSING UNDER PLASTIC LINER ALLOWING ACID INTO COCKPIT. MORE FREQUENT INSPECTION RECOMMENDED.SDR 99ZZZX706Battery Box · leakingDURING ANNUAL INSPECTION, BATTERY ACID WAS FOUND TO HAVE LEAKED INTO COCKPIT ONTO LEFT RUDDER PEDAL, ATTACHING TUBING, AND GENERAL AREA BELOW PEDAL. ACID HAD FLOWED THROUGH CORRODED RIVET HOLE ONTO SEAT FOR CABIN HEAT AND DRIPPED INTO FLOOR AREA. SUBMITTER BSDR 98ZZZX2180Support · failedBOTH BATTERY SUPPORT BRACKETS WERE FOUND BROKEN DURING AN ANNUAL INSPECTION. THESE SUPPORT BRACKETS ARE ONLY INSTALLED WITH THE MANIFOLD BATTERY INSTALLATION. ITEM 12 OF PART'S LIST.SDR VJ9800170Battery Tray · corrodedE/E COMP BATTERY TRAY LT SIDE HAS CORROSION. REMOVED CORROSION IAW DC-9 SRM 51-10-3 MATERIAL LOSS WAS FOUND TO BE 100 PERCENT, OUT OF LIMITS IAW IAW DC-9 SRM 53-01 FIG 1. FABRICATED DOUBLER REPAIR FROM 2004 T3 .875 BY 1.875 X 3.875 IAW DC-9 SRM 53-01 FIG 2. SDR VJ9800147Battery Tray · corrodedBATTERY TRAY, LT SIDE, IN E/E COMPARTMENT CORRODED BEYOND LIMIT IAW DC9 SRM 53-01, FIG 1. REMOVED CORROSION IAW DC9 SRM 51-10-3. FABRICATED DOUBLER REPAIR FROM 2024T3, 7/8 BY 13/8 BY 35/8 INCHES, IAW DC9 SRM 53-01, FIG 2. TREATED, PRIMED AND INSTALLED IAW SDR 98ZZZX1084Battery Box · not groundedHELICOPTER HAS BATTERY BOX BOLTED TO COMPOSITE FIREWALL. BATTERY BOX IS NOT GROUNDED TO BATTERY. A REGULATOR RECTIFIER AND STARTER RELAY ARE GROUNDED TO BATTERY BOX. A SCREWDRIVER WAS ACCIDENTLY DROPPED INSIDE OF BATTERY BOX TOUCHING POSITIVE TERMINAL. SCRSDR 97ZZZX4525Drain Tube · leakingWHILE PERFORMING 100-HOUR INSPECTION, NOTICED DRAIN TUBE FROM BATTERY BOX HAD BEEN LEAKING ACID INTO REAR FUSELAGE. SUBMITTER STATED THIS BATTERY BOX IS MOUNTED RIGHT OVER CONTROL CABLES AND CABLES COULD BE DAMAGED.SDR 97ZZZX3383Vent · pluggedAT ANNUAL INSPECTION, NOTICED CORROSION ON THE MAIN ELECTRICAL CONTACTOR AND THE STARTER RELAY. SUSPECT THE BATTERY WAS VENTING OUT BY THE CABLES. CHECKING THE BATERY BOX VENT, IT WAS FILLED WITH MUD DAUBER LARVA. THIS AIRCRAFT HAD ACCUMULATED 36 HOURS SINCSDR 96ZZZX5223Support · crackedINSPECTION FOUND BATTERY SUPPORT CRACKED. SUSPECT CAUSE IS TIME IN SERVICE. SHOULD BE THICKER MATERIAL.SDR CA960708001Battery Box Tube · broken(CAN) BATTERY BOX DRAIN TUBE FOUND BROKEN AND HAD ALLOWED VAPOURS TO ENTER THE AREA UNDER THE BATTERY BOX AND CORRODE THE STRUCTURE.SDR COMA9610207Bolt · rustedDURING 2C INSPECTION, FOUND FORWARD INBOARD CORNER OF BATTERY COMPARTMENT AT FRAME 4 TO HAVE SIGNS OF CORROSION. FURTHER INSPECTION FOUND NOSE GEAR FORWARD DOOR, AFT HINGE, HARDWARE TO BE CORRODED. REPLACED HARDWARE AND CLEANED BATTERY COMPARTMENT.SDR 96ZZZX2059Support · crackedTHE SUPPORTS THAT HOLD THE BATTERY WERE FOUND CRACKED. SEPARATION OF THESE SUPPORTS WOULD CAUSE THE BATTERY TO MOVE AROUND BEHIND THE REAR BULKHEAD, POSSIBLY GOING INTO CONTROL CABLES OR SHORTING THE ELECTRICAL SYSTEM. SUBMITTER STATED THIS IS THE THIRD AIRCSDR 96ZZZX1540Support · crackedBOTH BATTERY HOLD-DOWN SUPPORTS WERE FOUND CRACKED DURING A ROUTINE INSPECTION. CRACKS WERE AT BOTH ENDS OF THE SUPPORTS AND APPROXIMATELY 1 INCH IN LENGTH. SUBMITTER STATED THIS IS THE SECOND AIRCRAFT FOUND WITH THIS DEFECT. IF FAILURE HAD OCCURED, BATTERYSDR 95ZZZX2318Battery Vent · looseBATTERY ACID IN BELLY OF AIRCRAFT FROM BATTERY BOX FORWARD. CAUSED FROM BATTERY BOX OVERBOARD VENT DISCONNECTING FROM BOX WHEN BATTERY IS REMOVED. OVERBOARD VENT SHOULD BE CLAMPED TO BATTERY BOX TO PREVENT PROBLEM.SDR MALA954351Tray · crackedMSP - DURING A SCHEDULED INSPECTION, MECHANICS FOUND RT BATTERY SUPPORT TRAY ASSEMBLY (PN 27-82366-904) CRACKED. COMPLETED REPAIR BY THE PART FOR PART REPLACEMENT OF THE BATTERY SUPPORT TRAY ASSEMBLY IAW THE FAIRCHILD SRM. (X)
Back to JASC 2571