Cessna A152

Service difficulty reports · 56

Newest first. General aviation reporting is voluntary.

Query with SQL
duckdb -csv -c "SELECT sdr_id, difficulty_date, n_number, aircraft_make, aircraft_model, part_name, part_condition, jasc_code, discrepancy
  FROM 'https://openairdocs.org/data/latest/faa_service_difficulty_report.parquet'
  WHERE aircraft_model_key = 'A152'
  ORDER BY difficulty_date DESC"

Prints the whole list as CSV. It reads the release’s Parquet files over HTTPS, so there’s nothing to download first. Install DuckDB to run it.

SDR 8HBR20190613022Switch · failedDURING CRUISE CHECK LIST, STUDENT TRIED TO TURN LANDING LIGHT OFF BUT HE SAID IT GOT STUCK AND HE COULDN'T PUSH IT DOWN TO THE OFF POSITION, THE SECOND TIME HE TRIED TO PUSH IT DOWN IT WAS STILL STUCK BUT THAT'S WHEN HE SAW SPARKS AND SMOKE. STUDENT LEFT THE LJun 12, 2019 · Cessna A152 · Exterior LightingSDR 2015FA0000240Piston · brokenREMOVED NR 3 CYLINDER DUE TO LOW COMPRESSION, 62/80 PSI, AND FOUND 1"X.5" PIECE MISSING FROM PISTON SKIRT.May 14, 2015 · N4960A · Cessna A152 · Reciprocating Engine Power SectionSDR CA090717006Hub · unserviceable(CAN) DURING INSP, IAW AD 2003-12-05, CORROSION WAS FOUND IN THE HUB BORE. UPON DIMENSIONAL INSP OF BORE AND CONSULTATION WITH THE MFG IT WAS DETERMINED THAT THE BORE WAS OVERSIZE BY 0.230 INCH.Jul 15, 2009 · Cessna A152 · Propeller Hub SectionSDR M2Z2008F00000Battery Pack · leakingBATTERY PACK LEAKING. PREMATURE DEAD BATTERY. DESTROYED ELT. DEFECTIVE BATTERY AND/OR IMPROPER MFG PROCESS OF BATTERY PACK. (K)Oct 21, 2008 · N4958A · Cessna A152 · Emergency Locator BeaconSDR AU510001979Spar · corrodedRT WING SPAR CHANNEL HEAVILY CORRODED IN AREAS ON THE MATING FACE BETWEEN THE CHANNEL AND THE SPAR ANGLE.Dec 12, 2005 · Cessna A152 · Wing SparSDR AU510001978Angle · corrodedRT WING SPAR ANGLE CONTAINED AREAS OF HEAVY CORROSION BETWEEN THE MATING FACES OF THE ANGLE AND SPAR CHANNEL AND THE ANGLE AND THE SPAR STRAP. CORROSION WAS MAINLY LOCATED IN THE AREA OF THE TANK BAY.Dec 12, 2005 · Cessna A152 · Wing SparSDR AU510001977Spar · corrodedRT WING SPAR STRAP CONTAINED AREAS OF HEAVY CORROSION BETWEEN THE MATING FACES OF THE SPAR ANGLE AND SPAR STRAP LOCATED MAINLY IN THE TANK BAY AREA.Dec 12, 2005 · Cessna A152 · Wing SparSDR AU510001919Bracket · cracked(AUS) HORIZONTAL STABILIZER UPPER PLATE CRACKED IN AREA ADJACENT TO VERTICAL STABILIZER BRACKET ATTACHMENT. CRACK LENGTH 7MM (0.275IN). (AD/SB DESC: SEB 03-6 ) (CASA NR 510001919)Sep 9, 2005 · Cessna A152 · Horizontal Stabilizer, Spar/RibSDR AU510001918Bracket · crackedHORIZONTAL STABILIZER UPPER PLATE CRACKED IN AREA ADJACENT TO VERTICAL STABILIZER BRACKET ATTACHMENT. CRACK LENGTH 5MM (0.196IN).Aug 9, 2005 · Cessna A152 · Horizontal Stabilizer Miscellaneous StructureSDR CA050308004Rib · cracked(CAN) LEADING EDGE, LT IB RIB WAS FOUND CRACKED AT THE TOP REAR CORNER (RADIUS).Jan 10, 2005 · Cessna A152 · Horizontal Stabilizer, Spar/RibSDR CA040629008Plug · worn(CAN) A FEW PIECES OF NON-FERROUS MATERIAL WERE FOUND AT 1375.8 HOURS. FILTER RE-INSPECT SCHEDULED. SUBSEQUENT FILTER INSPECTION SHOWED HEAVY CONTAMINATION. ALL CYLINDERS REMOVED, FOUND PISTON PINS AND PLUGS NOT FLOATING. TWO PLUGS WERE WORN EXTENSIVELY. Jun 17, 2004 · Cessna A152 · Reciprocating Engine Power SectionSDR CA040622006Bracket · cracked(CAN) THE BRACKET OF THE STABILIZER ASSEMBLY WAS FOUND CRACKED.Jun 11, 2004 · Cessna A152 · Horizontal Stabilizer, Attach FittingsSDR AUS20040207Bracket · cracked(AUS) HORIZONTAL STABILIZER STEEL BRACKET CRACKED. CRACK LENGTH 10MM(0.393IN).Mar 17, 2004 · Cessna A152 · Horizontal Stabilizer Miscellaneous StructureSDR AUS20040114Gear · broken(AUS) STARTER MOTOR BENDIX DRIVE GEAR DISINTEGRATED. ENGINE RING GEAR TEETH DAMAGED.Feb 13, 2004 · Cessna A152 · Engine StarterSDR AUS20040075Carburetor · faulty(AUS) CARBURETOR FAULTY.Feb 5, 2004 · Cessna A152 · Fuel Control/Reciprocating EnginesSDR AUS20040082Alternator · failed(AUS) ALTERNAOR FAILED.Feb 3, 2004 · Cessna A152 · DC Generator-AlternatorSDR AUS20040074Drive Gear · stripped(AUS) ENGINE STARTER MOTOR DRIVE GEAR TEETH STRIPPED.Jan 5, 2004 · Cessna A152 · Engine StarterSDR AUS20030931Alternator · failed(AUS) ALTERNATOR FAILED.Sep 4, 2003 · Cessna A152 · DC Generator-AlternatorSDR AUS20030933Screw · loose(AUS) STARTER MOTOR INTERMEDIATE BEARING SECURING SCREW FELL OUT ANDSHORT CIRCUITED FIELD WINDINGS.Aug 29, 2003 · Cessna A152 · Engine StarterSDR AUS20030418Crankcase · cracked(AUS) CRANKCASE CRACKED BEYOND REPAIR AT LH CENTRE CAM JOURNAL BEARINGBASE. CRACK RUNS ACROSS THE JOURNAL SURFACE AND THEN DOWN FOR APPROXIMATELY 76.2MM (3IN) BEFORE TRAVELLING FOR ANOTHER 76.2MM (3IN) REARWARDS. SUMP INDUCTION TUBES LOOSE. THREE CYLINDERS CRAApr 1, 2003 · Cessna A152 · Reciprocating Engine Power SectionSDR 2003FA0000095Bracket · crackedDURING AN INSPECTION FOR AD (CRACKED NUT PLATES) THE BRACKET WHICH HOLDS THE NUT PLATES WAS FOUND CRACKED ON THE UPPER RIGHT HAND SIDE FROM THE CORNER RELIEF HOLE, INBOARD FOR APPROXIMATELY ONE INCH ALONG THE TOP BEND. THIS CRACK IS DIRECTLY ADJACENT TO AND JJan 3, 2003 · N8144L · Cessna A152 · Fuselage Miscellaneous StructureSDR AUS20021293Bellcrank · damaged(AUS) LT AILERON BELLCRANK STOP BENT. DAMAGE ALSO TO PUSH-PULL ROD AND ATTACHMENT HARDWARE AS WELL AS TO THE AILERON CONTROL BRACKET AND SECURING RIVETS.Nov 4, 2002 · Cessna A152 · Aileron Control SystemSDR CA021105009Rib · cracked(CAN) L/H INBOARD LEADING EDGE RIB WAS FOUND CRACKED AT THE TOP REAR CORNER OF THE HORIZONTAL STABILIZER.Nov 1, 2002 · Cessna A152 · Horizontal Stabilizer, Spar/RibSDR CA021105008Mount · cracked(CAN) ENGINE MOUNT CRACKED AT RT TOP AT THE WELDED JOINT.Nov 1, 2002 · Cessna A152 · Engine Mount SectionSDR AUS20020751Bracket · cracked(AUS) STEEL BRACKET ASSEMBLY CRACKED IN TWO PLACES. ONE CRACK LOCATED AT WELD SEAM AND ONE CRACK IN AREA OF ANCHOR NUT ATTACHMENT.BRACKET ATTACHES VERTICAL FIN TO TAILPLANE AND TAILPLANE TO FUSELAGE.Jul 12, 2002 · Cessna A152 · Fuselage, Stabilizer Attach FittingsSDR AU000897Engine · power loss(AUS) ENGINE LOST POWER. GROUND RUN CARRIED OUT WITH NO FAULT FOUND. (X)Sep 22, 2000 · Cessna A152 · Engine (Reciprocating)SDR CA000222006Horn · bent(CAN) DURING INSPECTION BY TRANSPORT CANADA INSPECTOR, THE RIGHT ARM OF THE RUDDER HORN WAS FOUND BENT, ALLOWING THE ATTACHED STOP PLATE TO RIDE UP AND OVER THE RUDDER STOP BOLT. THIS CAUSES THE RUDDER TO OVER TRAVEL WHEN FULL RUDDER DEFLECTION IS COMMANDED AFeb 15, 2000 · Cessna A152 · Rudder StructureSDR AU000101Fuel Tank · contaminated(AUS) AIRCRAFT FUEL SYSTEM CONTAMINATED WITH WATER. THE FUEL SYSTEM HAD BEEN FLUSHED WITH WATER IAW AD/GEN/80A1 FOLLOWED BY APPROVED PURGING OF THE WATER FROM THE SYSTEM. COMPLETE ENGINE FAILURE OCCURRED IN-FLIGHT. WHEN THE GASCOLATOR WAS DRAINED AFTER LANDIFeb 14, 2000 · Cessna A152 · Aircraft Fuel SystemSDR AU991013Blade · corroded(AUS) PROPELLER BLADE CONTAINED EXFOLIATION CORROSION. AREA OF CORROSION APPROXIMATELY 6 MM (0.236 INCH) BY 4 MM (0.157 INCH) BY 1 MM (0.039 INCH) DEEP. THE PROPELLER WAS INSTALLED NEW ON THE 7/14/99.Oct 15, 1999 · Cessna A152 · Propeller Blade SectionSDR 99ZZZX2029Filter · brittleDURING ROUTINE INSPECTION, FOUND VACUUM FILTER END CRUMBLING. FILTER WAS AT ITS 400 HOUR DUE TIME. WHEN PIECES OF RUBBER WERE REMOVED AND ROLLED BETWEEN FINGERS, THEY CRUMBLED INTO SMALL PIECES. HAVE FOUND SEVERAL LIKE THIS.Apr 16, 1999 · N7332L · Cessna A152 · Vacuum Distribution SystemSDR AU981572Rib · cracked(AUS) RIGHT WING NOSE RIB LOCATED AT WS 84.00 CRACKED.Nov 30, 1998 · Cessna A152 · Wing, Rib/BulkheadSDR AU981571Rib · cracked(AUS) LT WING NOSE RIBS LOCATED AT WS 84.00 CRACKED.Nov 30, 1998 · Cessna A152 · Wing, Rib/BulkheadSDR AU981378Skin · cracked(AUS) RIGHT WING UPPER SKIN CRACKED FROM RIVETS ATTACHING RIBS TO THE SKIN AT THE FOLLOWING LOCATIONS: 1. STN 84.0 - ON CRACK 2. STN 102.0 - TWO CRACKS. MAXIMUM CRACK LENGTH 3 MM (0.118 INCH). PART TC: 13,936.Oct 23, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981377Skin · cracked(AUS) LEFT WING UPPER SKIN CRACKED FROM RIVETS ATTACHING RIBS TO THE SKIN AT THE FOLLOWING LOCATIONS: 1. STN 84.0 - ONE CRACK. 2. STN 102.0 - ONE CRACK. MAXIMUM CRACK LENGTH 3 MM (0.118 INCH). PART TC: 13,936.Oct 23, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981321Skin · cracked(AUS) RIGHT UPPER WING SKIN CRACKED FROM RIVETS ATTACHING THE SKIN TO THE WING RIBS. SKIN CONTAINED TWO CRACKS LOCATED AT STN 84.0. MAXIMUM CRACK LENGTH 4 MM (0.157 INCH). PART TC: 6,516.Oct 9, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981320Skin · cracked(AUS) LEFT WING UPPER SKIN CRACKED FROM RIVETS ATTACHING THE SKIN TO THE WING RIBS. SKIN CONTAINED THREE CRACKS LOCATED AT STN 102.0 AND ONE CRACK LOCATED AT STN 84.0. PART TC: 6,516.Oct 9, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981319Skin · cracked(AUS) RIGHT WING UPPER SKIN CRACKED FROM RIVETS ATTACHING THE SKIN TO THE WING RIBS. ONE CRACK LOCATED AT STN 102.0 AND ONE CRACK LOCATED AT STN 84.0. MAXIMUM LENGTH OF CRACKS 3 MM (0.118 INCH). PART TC: 14,730.Oct 8, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981318Skin · cracked(AUS) LEFT WING UPPER SKIN CRACKED FROM RIVETS ATTACHING SKIN TO THE WING RIBS AT STN 102.0. MAXIMUM CRACK LENGTH 3 MM (0.118 INCH). PART TC: 14,730.Oct 8, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981191Skin · cracked(AUS) RIGHT UPPER WING SKIN CRACKED FROM THE RIVETS ATTACHING THE SKIN TO THE RIBS AT THE FOLLOWING LOCATION: THREE CRACKS LOCATED AT STN 102.0. MAXIMUM CRACK LENGTH 4 MM (0.157 INCH). PART TC: 14,010.Sep 21, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981190Skin · cracked(AUS) LEFT WING UPPER SKIN CRACKED FROM THE RIVETS ATTACHING THE SKIN TO THE RIBS AT THE FOLLOWING LOCATIONS: TWO CRACKS LOCATED AT STN 102.02. ONE CRACK LOCATED AT STN 84.0. MAXIMUM LENGTH OF CRACKS 4 MM (0.157 INCH). 14,010.Sep 21, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981181Skin · cracked(AUS) LEFT WING UPPER SKIN CRACKED IN THREE PLACES FROM SKIN TO RIB ATTACHMENT RIVETS: TWO CRACKS AT STN 102.0 . ONE CRACK AT STN 84.0. MAXIMUM LENGTH OF CRACKS 4 MM (0.157 INCH). PART TC: 15,720.Sep 18, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981180Skin · cracked(AUS) RIGHT WING UPPER SKIN CRACKED IN TWO PLACES FROM SKIN TO RIB ATTACHMENT RIVETS: ONE CRACK AT STN 102.0. ONE CRACK AT STN 84.0. MAXIMUM LENGTH OF CRACKS 4 MM (0.157 INCH). PART TC: 15,720.Sep 18, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981177Skin · cracked(AUS) UPPER LEFT WING SKIN CRACKED IN TWO AREAS BETWEEN THE FRONT AND REAR SPARS. UPPER RIGHT WING SKIN CRACKED IN TWO AREAS STARTING FROM THE RIVETS ATTACHING THE SKIN TO THE WING RIB AT WS 102. MAXIMUM CRACK LENGTH 3 MM (0.118 INCH). PART TC: 9,847.Sep 17, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU981155Skin · cracked(AUS) LEFT WING UPPER SKIN CRACKED IN THREE LOCATIONS BETWEEN THE FRONT AND REAR SPARS. CRACKS ORIGINATE FROM THE RIVETS ATTACHING THE SKIN TO THE WING RIB AT STN 102. MAXIMUM CRACK LENGTH 4 MM (0.157 INCHES). PART TC: 7,047.Sep 11, 1998 · Cessna A152 · Wing, Plate/SkinSDR AU980332Plate · corroded(AUS) WING SPAR PLATE CONTAINED EXFOLIATION CORROSION BETWEEN SPAR FLANGE AND SPAR PLATE. LENGTH OF CORROSION 35MM (1.37 INCH).Mar 17, 1998 · Cessna A152 · Wing SparSDR CA970507010Bar · broken(CAN) DURING A PRACTICE SPIN RECOVERY, NO RIGHT RUDDER CONTROL WAS AVAILABLE FROM THE LEFT SEAT POSITION. THE AIRCRAFT WAS FLOWN FROM THE RIGHT SEAT AND LANDED SAFELY. MAINTENANCE FOUND THE LEFT SIDE RIGHT RUDDER PEDAL BROKEN OFF THE TORQUE TUBE BELOW THE WEApr 23, 1997 · Cessna A152 · Rudder Control SystemSDR AU970246Floor · cracked(AUS) FLOOR CRACKED IN AREA OF SEAT RAIL ATTACHMENT AT REAR - SEAT RAIL HAS A RIGHT ANGLE END WHICH CUTS INTO FLOORMar 7, 1997 · Cessna A152 · Fuselage Floor PanelSDR AU970064Spar · cracked(AUS) LH ELEVATOR SPAR CRACKED FROM UPPER OUTBOARD BENDING RADIUS CUTOUT INBOARD ALONG VERTICAL FACE OF SPAR PASSING ADJACENT TO UPPER RIVET ATTACHING HINGE HALF PNO 0432001-71 - CRACK LENGTH38MM (1.49IN) - DURING REPAIR ANOTHER CRACK WAS FOUND EXTENDING BELOWJan 23, 1997 · Cessna A152 · Elevator, Spar/RibSDR AU961210Hub · cracked(AUS) PROPELLER HUB CRACKED ADJACENT TO BOLT HOLES AS INDICATED IN MCCAULEY SB 219Aug 23, 1996 · Cessna A152 · Propeller Hub SectionSDR 96ZZZX4231Hose · deteriorated1981 - 1,425 HOURS TT. TOTAL DETERIORATION OF OUTER LAYER, REINFORCING THREADS, AND INNER LAYER. HOSE IS OF A PLASTIC TYPE, APPEARS TO BE ORIGINAL. REPLACED WITH AEROQUIP 306 INSTRUMENT HOSE.Aug 2, 1996 · N152J · Cessna A152 · Flight Environment Data
Back to Cessna A152