OUTER EDGE OF DOUBLER
BUTT JOINT OF PATCH TO SKIN
INNER EDGE OF DOUBLER
NAIL HOLES -
D SCREW HOLES -
TO BE FILLED BEFORE
FINISHING
PATCH DIMENSIONS
A B C D E F SMALL 1-1/2 2-1/8 |1-1/2 718 3 4-1/2 LARGE 2 3-3/8 2-1/2 1-5/8 7
TWO ROWS OF SCREWS AND
NAILS REQUIRED ON LARGE BUTT JOINT OF PATCH TO SKIN PATCH.
PLYWOOD DOUBLER (GRAIN PARALLEL TO SKIN) >E- (LAMINATE DOUBLER FROM TWO МАШЕТ "14" PIECES OF 1/8" PLY IN AREAS OF
- PLUG PATCH (GRAIN PARALLEL TO SKIN) SKIN CURVATURE,)
PLYWOOD SKIN FIGURE 1-17. Oval plug patch assembly.
Par 1-54 Page 1-32
GRAIN DIRECTION OF SKIN, PATCH, AND DOUBLER.
- SAW CUT IN DOUBLER.
BUTT JOINT OF PATCH TO SKIN.
INNER EDGE OF DOUBLER.
• OUTER EDGE OF DOUBLER.
NAIL HOLES -
SCREW HOLES - TO BE FILLED BEFORE FINISHING.
BUTT JOINT OF PATCH TO SKIN - PLUG PATCH
PLYWOOD SKIN - SAW CUT IN DOUBLER PLYWOOD DOUBLER (LAMINATE DOUBLER FROM TWO PIECES OF 1/8" PLY IN AREAS OF SKIN CURVATURE.)
DIMENSIONS B C SMALL CIRCULAR PLUG PATCH 2 6/8 1 3/8 LARGE CIRCULAR PLUG PATCH 3 718 2 1/8 (TWO ROWS OF SCREWS AND NAILS REQUIRED
FOR LARGE PATCH) FIGURE 1-18. Round plug patch assembly.
1-53.-1-63. [RESERVED.] Par 1-52 Page 1-33 (and 1-34)
Par 1-64 Page 1-34
SECTION 5. FINISHING WOOD STRUCTURES
GENERAL. Any repair to spars, ribs, skin surfaces, or other structural parts of the airframe involves finishing as the final step of the job. The surface finish is the final line of defense to prevent the destructive effects of moisture entry into the structure. The time and effort spent during the preparatory phase of the refinishing process will be reflected in the appearance and longevity of the finished surface. Adherence to the instructions issued by the finish manufacturer is necessary to obtain the appearance desired and protective characteristics for the product used. The primary objective of interior finishes is to afford protection of the wood against serious change in moisture content when exposed to damp air or to water that gains entrance to closed spaces by condensation or by penetration of rain, mist, or fog. Coatings, on contact areas between wood and metal protect the metal against corrosion from moisture in the wood.
The primary objectives of the exterior finish are to protect the wood against weathering, provide a suitable appearance, and present a smooth surface in flight.
ACCEPTABLE FINISHES. Any varnish conforming to Federal Specification TT-V-109, as amended, or other coating approved by the airframe manufacturer or the FAA is acceptable. Exterior surfaces must be further protected from the effects of abrasion, weather, and sunlight. A number of systems for exterior finishing have STC approval and are manufactured under a PMA. (See CChapter 2, Fabric Covering.) Low viscosity epoxy adhesive (meeting the requirements of paragraph 1-4 for that purpose) may be used as an internal surface finish when subsequent bonding is necessary.
PRECAUTIONS.
When making repairs, avoid excessive contamination of surfaces with adhesive squeeze-out at joints and on all surfaces. Excess adhesive should always be removed before appl ying finish. Because many paints and adhesives are incompatible, even a slight amount of adhesive underneath the finish may cause premature deterioration of the finish.
Soiling substances, such as oil and grease, should be removed as completely as possible. Naphtha may be used to remove surface deposits of oil and grease;
however, thinned residue may penetrate into any unprotected wood. In areas where minor amounts of oil or grease have penetrated the wood surface, removal may be accomplished by use of an absorbent type of cleaner such as gunsmith's whiting or a clothing spot lifter such as K2r . Marks that are made by grease pencils or lumber crayons containing wax are harmful and should be removed, but marks made by ordinary soft graphite pencils and nonoily stamp pad inks may be safely finished over. All dust, dirt, and other solid particles should be removed.
Sawdust, shavings, and chips must be removed from enclosed spaces before they are sealed off by replacement of skin. A vacuum cleaner is useful for such cleaning.
Since most adhesives will not bond satisfactorily to sealers, it is necessary to avoid applying sealer over the areas where adhesive will be applied. Mark off areas to receive adhesive, and allow an additional 1/4 inch on each side of the adhesive area to provide for
Par 1-69 1-35 misalignment when mating the parts. It is preferable to leave some unsealed areas ra ther than risk weakening the joint by accidental overlap of the sealer into the bonded areas. Wherever possible, apply sealer to the margins after the adhesive has cured. As an example, the lower skin of a wing bay would be installed first, leaving access from above to apply sealer. All low spots (where moisture would collect) are well sealed.
The top skin would be installed last, so that the only unsealed margins would be on upper surfaces where moisture is least likely to collect.
An alternative to the previous paragraph is to use an approved epoxy coating and compatible epoxy adhesive. Apply the coating, allowing 1/4 inch margins as in the previous paragraph. After the coating has cured, apply epoxy adhesi ve to joint surfaces, and overlap the adhesive onto the sealer. Close joint and clamp. The epoxy adhesive will bond satisfactorily to the coating and ensure a complete coverage of the wood surfaces. Use only approved and compatible adhesives and coatings for this method.
FINISHING OF INTERIOR SURFACES. Finish repaired ribs, spars, interior of plywood skin, and other internal members, including areas of contact between metal and wood, by applying one thinned coat (for penetration into wood grain) of varnish or other acceptable finish, followed by two full coats. Protect built-up box spars and similar closed structures on the interior in the same way. Where better protection is required, as on the surfaces of wheel wells and the bottoms of hulls below the floor boards, an additional coat of aluminized sealer consisting of 12 to 16 ounces of aluminum paste per gallon of sealer, may be applied.
FINISHING OF EXTERIOR SURFACES. Exterior surfaces require more protection than interior areas due to the effects of abrasion, weather, and sunlight. (See chapter 2.) Tests have shown that the interior temperature of wooden aircraft structures can reach 185 ºF when the aircraft is finished in a dark color and parked outdoors on a hot, still day. Exposure to prolonged high temperature is detrimental to wood, adhesives, and finishes. Wood loses approximately 25 percent of its strength at 125 ºF. For this reason, the mechanic should consider temperature effects when selecting finish colors or looking for areas of likely deterioration. The lowest temperatures are found when the aircraft is finished in white or very light colors, while darker colors produce higher temperatures. A general trend toward higher temperatures may be seen when exterior colors are yellow, pink, light blue, aluminum, purple, blue, light green, orange, tan, red, green, brown, and black. A lighter shade of a particular color helps to reduce temperatures.
FINISHING OF END GRAIN SURFACES. End grain portions of wooden members are much more absorbent than side grain. Because of this extreme vulnerability to moisture entry, it is necessary to take extra precautions to seal end grain.
Apply at least one thinned coat of acceptable sealer to ensure maximum penetration, and then follow with as many full strength coats as necessary to achieve a smooth, glossy coating. Depending on the type wood to be finished, two to four full coats will be required. A final coat of aluminized varnish may be applied to end grain surfaces. If the surfaces are to be finished with dope or lacquer, a dope-proof sealer, similar to Federal Specification TT-V-109, or epoxy sealer should be used.
Exposed end grain includes such surfaces as spar butts, skin edges, areas around vent holes, inspection holes, fittings, and exposed scarfed or tapered surfaces.
Par 1-70 Page 1-36 (and 1-38) FINISHING WITH FABRIC OR TAPE. A number of systems for exterior finishing have STC approval and are manufactured under a PMA.
Follow the product manufacturer's instructions for the system used.
If the finish surrounding the repair is a traditional dope system, seal the wood grain with a suitable solvent resistant one-part varnish, commonly described as “dope proof,” or a two-part epoxy varnish. Follow with two coats of clear dope, and allow sufficient drying time between coats.
Apply a third coat of clear dope and lay a piece of pinked-edge airplane cloth into the wet film. All air bubbles should be worked out by brushing to ensure maximum adhesion. When dry, apply one brush coat, to ensure proper penetration, and at least one spray coat of clear dope. The dried spray coat may be sanded with fine sandpaper to obtain a smoother finish. Complete the refinishing of the surface by application of a topcoat as required to match the adjacent area.
SEALING OF BOLT HOLES. Bolt holes in wooden structure provide a vulnerable entry point for moisture. Variations in moisture content around bolt holes can lead to decay or splitting. In addition, excessive moisture at bolt holes promotes corrosion of the bolts.
Sealing of the wood surfaces in bolt holes can be accomplished by application of varnish or other acceptable sealer into the open hole. The sealer must be allowed to dry or cure thoroughly prior to bolt installation.
1-72.1-79. [RESERVED.]
Par 2-1 Page 2-37
CHAPTER 2. FABRIC COVERING
SECTION 1. PRACTICES AND PRECAUTIONS
GENERAL. Cotton and Irish linen fabrics were the airframe coverings of choice from WWI through the 1950’s. However, increases in cost and the short lifespan of natural fabrics became the driving factors which resulted in almost 100 percent replacement of original airframe fabrics by man-made, STC-approved, polyester, and glass filament fabric.
PROBLEM AREAS.
Deterioration. Polyester fabric deteriorates only by exposure to ultraviolet radiation as used in an aircraft covering environment. When coatings completely protect the fabric its service life is infinite. Therefore, it is very important to thoroughly protect the structure from deterioration before covering and provide adequate inspection access to all areas of fabric-covered components to allow inspection for corrosion, wood rot, and mice infestation. Multiple drain holes in the lower ends of all fabric-covered s ections also provide needed ventilation to remove condensation.
Tension. Polyester fabric obtains maximum tension on an airframe at 350 ºF, and will not be excessive on aircraft originally covered with natural fabric and 12 coats of Nitrate or Butyrate Dope. However, dope applied over full heat-tauted fabric can develop excess tension after aging and damage light aircraft structures.
Coatings other than dope will not increase fabric tension after aging. The heat-tauting instructions given in the manual of each STC-approved covering process should be followed.
AIRCRAFT FABRIC-SYNTHETIC.
STC-Approved Covering Materials. There is a wide selection of STC-approved covering materials available which utilize synthetic fabric falling within the generic class “Polyester” and may vary in characteristics.
Difference in the fabric may be denier, tenacity, thread count, weight, shrink, tension, and weave style.
Polyester Filaments. Polyester Filaments are manufactured by polymerization of various select acids and alcohols, then extruding the resulting molten polymers through spinnerets to form filaments. The filaments are heat stretched to reduce to the desired denier or size. It is the heat stretching that imparts a memory in the filaments causing them to try and return to their original shorter length when reheated at a controlled temperature. Overheating will cancel the memory and melt the filaments.
Covering Procedures. Coating types, covering accessories, and covering pro cedures also may vary;
therefore, the covering procedures given in the pertinent manuals must be followed to comply with the STC.
The FAA STC-approved installation takes precedence over instructions in this advisory circular.
Installation. Initial installation of polyester fabric is similar to natural fabric. The fabric is installed with as little slack as possible, considering fittings and other protrusions. It may be sewn into an envelope, installed as a blanket, or installed by cementing to the airframe with a fabric cement. E ach STC may differ in the cement seam overlap, type of sewn seam, heat shrinking procedures, and temperature.
Par 2-1 Page 2-38 AIRCRAFT FABRIC-NATURAL. Physical specifications and minimum strength requirements for natural fiber fabric, cotton and linen, used to recover or repair components of an aircraft, are listed in table 2-1. Tear resistance is an important factor when considering aircraft fabric. A test method such as ASTM D 1424 is recommended. Technical Standard Order TSO-C15d, entitled Aircraft Fabric, Grade A (AMS 3806D); and TSO-C14b, Aircraft Fabric, Intermediate Grade (AMS 3804C) current edition, respectively, describe the minimum standards that all fabric must meet to qualify as aircraft covering material.
RECOVERING AIRCRAFT. Recover or repair aircraft with a fabric of equal quality and strength to that used by the original aircraft manufacturer. It is recommended that fabric conforming to TSO-C15d or TSO-C14b be used to recover aircraft originally covered with lower strength fabric conforming to AMS 3802, current edition.
NOTE: Recovering or repairing aircraft with any type fabric and/or coating other than the type used by the original aircraft manufacturer is considered a major alteration. Obtain approval from the FAA on fabric and installation data. Cotton and linen rib lacing cord, mach ine and hand-sewing thread, and finishing tapes should not be used with polyester and glass fabric covering.
Reinforcing tape minimum tensile strength is listed in table 2-2. Reinforcing tape meeting specification MIL-T-5661, Type I, current edition, is acceptable.
Reinforcing tape should have a minimum 40 lb.
resistance without failure when static tested in shear against a single rib lace, or a pull-through resistance when tested against a single-wi re clip, rivet, screw, or any other type of fabric-to-rib attachment. Reinforcing tape is used over the rib cab on top of the fabric and for inter-rib bracing.
Finishing Tape, sometimes referred to as surface tape, should have the same properties as the fabric used to cover the aircraft.
Lacing Cord shall have a minimum breaking strength of 40 lb. Lacing cord meeting the specifications listed in table 2-2 is acceptable. Rib lace cord should have a microcrystalline fungicidal wa x, paraffin-free wax, or beeswax coating, or other approved treatment to prevent wearing and fraying when pulling through the structure.
Machine Thread shall have a minimum breaking strength of 5 lb. Thread meeting the specifications listed in table 2-2 is acceptable.
Hand-Sewing Thread shall have a minimum breaking strength of 14 lb. Thread meeting the specifications listed in table 2-2, is acceptable. When covering with STC-approved fabric covering material, use the type of sewing thread approved by the STC and manufactured under the specific PMA.
Flutter Precautions. When re-covering or repairing control surfaces, especially on high performance airplanes, make sure that dynamic and static balances are not adversely affected. Weight distribution and mass balance must be considered to preclude to possibility of induced flutter.
PREPARATION OF THE STRUCTURE FOR COVERING. One of the most important items when covering aircraft is the proper preparation of the structure. Before covering, the airframe must be inspected and approved by a FAA-certified mechanic or repair station.
Par 2-6 Page 2-39 TABLE 2-1. Cotton and linen fabrics.
Materials
Specification Minimum Tensile Strength New (undoped) Minimum Tearing Strength New (undoped) (ASTM D 1424) Minimum Tensile Strength Deteriorated (undoped)
Thread Count Per Inch
Use and Remarks
Airplane cloth mercerized cotton (Grade “A”).
TSO-C15d, as amended, references Society Automotive Engineers AMS 3806d, as amended or MIL-C-5646
80 pounds per inch warp and fill.
5 pounds warp and fill.
56 pounds per inch.
80 min., 84 max.
warp and fill.
For use on all aircraft.
Required on aircraft with wing loading of 9 p.s.f. or greater or placard never exceed speed of 160 m.p.h.
or greater.
Airplane cloth mercerized cotton.
TSO-C14b, as amended, references Society Automotive Engineers AMS-3804c, as amended.
65 pounds per inch warp and fill.
4 pounds warp and fill.
46 pounds per inch.
80 min., 94 max.
warp and fill.
For use on aircraft with wing loading less than 9 p.s.f. and never exceed speed of less than 160 m.p.h.
Airplane cloth mercerized cotton.
Society Automotive Engineers AMS 3802, as amended.
50 pounds per inch warp and fill.
3 pounds warp and fill.
35 pounds per inch.
110 max.
warp and fill.
For use on gliders with wing loading of 8 p.s.f. or less, provided the placarded never-exceed speed is 135
m.p.h. or less.
Aircraft linen.
British 7F1.
This material meets the minimum strength requirements of TSO-C15.
Battery Box Treatment. An asphaltic, rubber-based acid-proof coating should be applied to the structure in the area of a battery box, by brush, for additional protection from battery acid. Control cables routed in the area of the battery box should be coated with paralketone.
Worn Holes. Oversized screw holes or worn size 4 self-tapping screw holes through ribs and other structures used to attach fabric may be redrilled a minimum 1-1/2 hole diameter distance from the original hole location with a # 44 (0.086) drill bit. Size 6 screws, drill bit size # 36 (0.1065), may be installed in stripped or worn holes drilled for size 4 sc rews, usually without redrilling. Worn holes for wire clips and wire barbs should be redrilled a minimu m 1-1/2 hole distance from the original locations using a drill jig to ensure correct spacing, with the appropriate size drill bit. Drill bit size # 30 (0.128) may be used to redrill oversize holes for 1/8-inch diameter blind rivets a minimum 1-1/2 hole diameter distance from the original location.
Par 2- Page 2-40 TABLE 2-2. Cotton and Linen, Tapes and Threads.
Materials
Specification
Yarn Size Minimum Tensile Strength Yards Per Pound
Use and Remarks
Reinforcing tape, cotton.
MIL-T-566 1 E, Type 1 MIL-Y-1140H
150 pounds per 1/2 inch width.
Used as reinforcing tape on fabric and under rib lacing cord. Strength of other widths approx. in proportion.
Lacing cord, prewaxed braided cotton.
Federal T-C-57 1F
40 pounds.
310 minimum.
Lacing fabric to structures. Unless already waxed, must be lightly waxed before using.
Lacing cord, braided cotton.
MIL-C-5648A
80 pounds.
170 minimum.
Lacing fabric to structures. Unless already waxed, must be lightly waxed before using.
Lacing cord thread, high tenacity cotton.
MIL-T-5660B
Ticket No.
10.
62 pounds.
480 minimum.
Lacing fabric to structures. Unless already waxed, must be lightly waxed before using.
Machine thread cotton Federal V-T- 276H
20/4 ply
5 pounds.
5,000 nominal.
Use for all machine sewing.
Hand-Sewing thread cotton.
Federal V-T- 276H Type III B
8/4 ply
14 pounds.
1,650 nominal.
Use for all hand-sewing.
Use fully waxed thread.
Finishing (Surface) tape cotton.
Same as fabric used.
Same as fabric used.
Use over seams, leading edges, trailing edges, outer edges and ribs, pinked, raveled or straight edges.
Fairing Precautions. Aluminum leading edge replacement fairings installed in short sections may telescope during normal spar bending loads or from thermal expansion and contraction. This action may cause a wrinkle to form in th e fabric, at the edge of the lap joint. Leading edge fairing sections may be fastened together with rivets or screws to prevent telescoping after installation. Trailing edges should be adequately secured to prevent movement and wrinkles.
Dope Protection . Solvents found in nitrate and butyrate dope will penetrate, wrinkle, lift, or dissolve most one-part wood varnishes and one-part metal primers. All wood surfaces th at come in contact with doped fabric should be treated with a protective coating such as aluminum foil, cellulose tape, or dope-proof paint to protect them against the action of the solvents in the dope. This can also be accomplished by recoating with a suitable, solvent resistant two-part epoxy varnish, which will be impervious to solvent penetration and damage after curing. Clad aluminum and stainless steel parts need not be dope-proofed.
A solvent-sensitive primer on ferrous metal and aluminum alloy components which will be in contact with fabric may be protected from solvent damage by overcoating with a two-part epoxy primer. Epoxy primer meeting MIL-P-53022B is acceptable.
Small metal or wood surfaces, such as rib caps, to which fabric will not be dope bonded as a part of the particular fabric attachment procedure may be protected from dope damage by cellophane tape or aluminum foil.
Chafe Protection. Fabric and finishing tape is often cut through with sandpaper over sharp edges during the coating and finishing procedure and later polishing. All sharp metal edges or protruding screws, nails, rivets, and bolt heads should be covered with an anti-chafe tape to prevent cutting and wearing through the fabric after installation. Use
Par 2-6 Page 2-41 appropriate non-bleeding cotton adhesive coated tape, finishing tape, or strips of fabric, cut from the fabric being used to cover the aircraft, doped in place.
Small holes cut through the fabric to accommodate flying wires, control cables, and fittings, must be reinforced with finishing tape or fabric patches cut from the same fabric used for the covering.
Areas needing additional chafe protection such as control cables routed firm against the fabric surface should be protected with patches cut from cotton duck, leather, or plastic. These patches may be sewn, doped, or cemented in place, as appropriate.
Any drag and anti-drag wires in the wings should be protected from chafing at cross points.
Inter-Rib Bracing. Use a woven fabric tape of the same quality and width as th at used for the rib lace reinforcing, where so incorporated in the wing design by the original aircraft manufacturer. When the original routing for the inter rib bracing is not known, the tape will be routed diagonally, a lternating between the top and bottom of each rib cap on each successive rib, if a single pair, half way between the front and rear spars.
The number of tape pairs will duplicate the original aircraft manufacturer’s installation. Tapes will be routed continuously from the wing butt to the wingtip bow, with one turn of tape around each intermediate rib cap strip. Care should be given to position the tape so as not to interfere with control cables, bellcranks or push-pull rods.
Preparation of Plywood Surfaces for Covering. Prior to covering plywood surfaces, prepare the surface by sanding, cleaning, and applying sealer and dope. When plywood surfaces are to be c overed with light weight glass fiber deck cloth instead of fabric, no sealer or dope should be applied to the plywood as it would inhibit penetration of epoxy resin.
Sand plywood surfaces as needed to remove old loose dope or varnish residue to provide a clean bonding surface. Remove any oil, grease, or other contamination with a suitable solvent such as naphtha. Small, rough areas and irregularities in the plywood surface and around any plywood repairs may be filled and smoothed with an appropriate commercial grade wood filler. Filling large warp depressions on plywood surfaces with a wood filler for cosmetic purposes is not acceptable.
After cleaning and sanding all plywood surfaces, seal the wood grain with a suitable solvent resistant two-part epoxy varnish. After the varnish has thoroughly dried, apply two brush or spray coats of clear dope, allowing sufficient drying time between coats.
FABRIC SEAMS. Seams parallel to the line of flight are preferable; however, spanwise seams are acceptable.
Sewn Seams.
Machine-sewn seams should be double stitched using any of the styles illustrated in figure 2-1 A, B, C, or D. A machine-sewn seam used to close an envelope at a wingtip, wing trailing edge, empennage and control surface trailing edge, and a fuselage longeron may be made with a single stitch when the seam will be positioned over a structure. (See figure 2-1 E.) The envelope size should accommodate fittings or other small protrusions with minimum excess for installation. Thick or protruding leading edge sewn seams should be avoided on thin airfoils with a sharp leading edge radius because they may act as a stall strip.
Par 2-6 Page 2-42 Hand sew, with plain overthrow or baseball stitches at a minimum of four stitches per inch, or permanent tacking, to the point where uncut fabric or a machine-sewn seam is reached. Lock hand sewing at a maximum of 10 stitch intervals with a double half hitch, and tie off the end stitch with a double half hitch. At the point where the hand-sewing or permanent tacking is necessary, cut the fabric so that it can be doubled under a minimum of 3/8 inch before sewing or permanent tacking is performed. (See figure 2-2.)
After hand sewing is complete, any temporary tacks used to secure the fabric over wood structures may be removed.
Cover a sewn spanwise seam on a wing’s leading edge with a minimum 4-inch wide pinked-edged surface tape with the tape centered on the seam.
Cover a spanwise-sewn seam at the wing trailing edge with pinked-edge surface tape that is at least 3 inches wide. For aircraft with never-exceed speeds in excess of 200 mph, cut V notches at least 1 inch in depth and 1/4 inch in width in both edges of the surface tape when used to cover spanwise seams on trailing edges of control surfaces. Space notches at intervals not exceeding 6 inches.
On tape less than 3 inches wide, the notches should be 1/3 the tape width. In the event the surface tape begins to separate because of poor adhesion or other causes, the tape will tear at a notched section, thus preventing progressive loosening of the entire length of the tape which could seriously affect the controllability of the aircraft. A loose tape acts as a trim tab only on a movable surface. It becomes a spoiler on a fixed surface and has no effect at the trailing edge other than drag.
Make spanwise-sewn seams on the wing’s upper or lower surfaces in a manner that will minimize any protrusions. Cover the seams with finishing tape at least 3 inches wide, centering the tape on the seam.
Sewn seams parallel to the line of flight (chordwise) may be located over ribs.
However, careful attention must be given to avoid damage to the seam threads by rib lace needles, screws, rivets, or wire clips that are used to attach the fabric to the rib. Cover chordwise seams with a finishing tape at least 3 inches wide with the tape centered on the seam.
Doped Seams.
For an overlapped and doped spanwise seam on a wing’s leading edge, overlap the fabric at least 4 inches and cover with finishing tape at least 4 inches wide, with the tape centered at the outside edge of the overlap seam.
For an overlapped and doped spanwise seam at the trailing edge, lap the fabric at least 3 inches and cover with pinked-edge surface tape at least 4 inches wide, with the tape centered on the outside edge of the overlap seam.
For an overlapped and doped seam on wingtips, wing butts, perimeters of wing control surfaces, perimeters of empennage surfaces, and all fuselage areas, overlap the fabric 2 inches and cover with a finishing tape that is at least 3 inches wide, centered on the outside edge of the overlap seam.
For an overlapped and doped seam on a wing’s leading edge, on aircraft with a velocity never exceed (Vne) speed up to and including 150 mph, overlap the fabric 2 inches and cover with a finishing tape that is at least 3 inches wide, with the tape centered on the outside edge of the overlap seam.
1/16" 3/8* - 1/16" 116→ 1114"→ 1/16"
STITCHING
•STITCHING A. PLAIN OVERLAP SEAM, STRAIGHT EDGE B. FRENCH FELL SEAM 1/16" 3/8" - 1/16" 1/4"
STITCHING C. FOLDED FELL SEAM
STITCHING STEP 1 1/16"-
•3/8** 1/16" STEP 2 STITCHING E. SINGLE STITCH SEAM TO CLOSE AN
ENVELOPE WHEN THE STITCH WILL
BE LOCATED OVER A STRUCTURE D. MODIFIED FOLDED FELL SEAM SEWN IN
TWO STEPS FIGURE 2-1. Fabric seams.
Par 2-7 Page 2-43